Study of high-quality epitaxial YBCO thin films grown directly on y-cut LiNbO₃

Pulsed laser deposition was used to deposit high-quality YBa₂Cu₃O_7-δ (YBCO) thin films directly on y-cut LiNbO₃ substrates. The as-deposited YBCO films had a high degree of in-plane orientation and showed superconducting transition temperature (T_co) at 91K with a transition width of less than 1K. Transport critical current densities were found to be ∼10⁶ A/cm² at 77K and zero field. An ion beam minimum channeling yield of 16% was obtained for YBCO films, indicating high crystallinity. High-resolution transmission electron microscopy studies showed that the interface between the film and the substrate was quite smooth and free from interfacial interdiffusion. The defects in thin films are also identified. The work showed that high-quality high T_c thin films can be deposited directly on LiNbO₃. Novel devices based on the properties of both YBCO and LiNbO₃ could be realized based on these results.