Properties of YBCO on LaMnO3-capped IBAD MgO-templates without homo-epitaxial MgO layer

Ö Polat; Tolga Aytug; Mariappan Paranthaman; Kyunghoon Kim; Yifei Zhang; Claudia Cantoni; Yuri L. Zuev; Amit Goyal; James R. Thompson; David K. Christen; Xuming Xiong; Venkat Selvamanickam

doi:10.1109/TASC.2009.2018815

Properties of YBCO on LaMnO₃-capped IBAD MgO-templates without homo-epitaxial MgO layer

Ö Polat
, Tolga Aytug
, Mariappan Paranthaman
, Kyunghoon Kim
, Yifei Zhang
, Claudia Cantoni
, Yuri L. Zuev
, Amit Goyal
, James R. Thompson
, David K. Christen
, Xuming Xiong
, Venkat Selvamanickam

Department of Chemical and Biological Engineering

Oak Ridge National Laboratory
University of Tennessee
Super Power Inc.

Research output: Contribution to journal › Article › peer-review

5 Scopus citations

Abstract

Previously, it has been well established that in an IBAD architecture for coated conductors, (1) LaMnO₃ (LMO) buffer layers are structurally and chemically compatible with an underlying homo-epitaxial MgO layer and (2) high current density YBCO films can be grown on these LMO templates. In the present work, the homo-epi MgO layer has been successfully eliminated and a LMO cap layer was grown directly on the IBAD-MgO template. The performance of the LMO/IBAD-MgO samples has been qualified by depositing 1 μm-thick YBCO coatings by pulsed laser deposition. Electrical transport measurements of YBCO films on the standard (with homo-epi MgO) and simplified (without homo-epi MgO) IBAD architectures were carried out. The angular dependence of critical current density (J_c) is similar for both IBAD architectures. XRD measurements indicate good, c-axis aligned YBCO films. Transmission electron microscopy (TEM) images reveal that microstructures of YBCO/LMO/IBAD-MgO and YBCO/LMO/homo-epi MgO/IBAD-MgO templates are similar. These results demonstrate the strong potential of using LMO as a single cap layer directly on IBAD-MgO for the development of a simplified IBAD architecture.

Original language	English
Article number	5153190
Pages (from-to)	3315-3318
Number of pages	4
Journal	IEEE Transactions on Applied Superconductivity
Volume	19
Issue number	3
DOIs	https://doi.org/10.1109/TASC.2009.2018815
State	Published - Jun 2009

Keywords

Buffers
Critical current density
IBAD-MgO
LMO
PLD-YBCO

Access to Document

10.1109/TASC.2009.2018815

Cite this

Polat, Ö., Aytug, T., Paranthaman, M., Kim, K., Zhang, Y., Cantoni, C., Zuev, Y. L., Goyal, A., Thompson, J. R., Christen, D. K., Xiong, X., & Selvamanickam, V. (2009). Properties of YBCO on LaMnO₃-capped IBAD MgO-templates without homo-epitaxial MgO layer. IEEE Transactions on Applied Superconductivity, 19(3), 3315-3318. Article 5153190. https://doi.org/10.1109/TASC.2009.2018815

@article{12225e4a20a64d21a1192a3061b11bcc,

title = "Properties of YBCO on LaMnO3-capped IBAD MgO-templates without homo-epitaxial MgO layer",

abstract = "Previously, it has been well established that in an IBAD architecture for coated conductors, (1) LaMnO3 (LMO) buffer layers are structurally and chemically compatible with an underlying homo-epitaxial MgO layer and (2) high current density YBCO films can be grown on these LMO templates. In the present work, the homo-epi MgO layer has been successfully eliminated and a LMO cap layer was grown directly on the IBAD-MgO template. The performance of the LMO/IBAD-MgO samples has been qualified by depositing 1 μm-thick YBCO coatings by pulsed laser deposition. Electrical transport measurements of YBCO films on the standard (with homo-epi MgO) and simplified (without homo-epi MgO) IBAD architectures were carried out. The angular dependence of critical current density (Jc) is similar for both IBAD architectures. XRD measurements indicate good, c-axis aligned YBCO films. Transmission electron microscopy (TEM) images reveal that microstructures of YBCO/LMO/IBAD-MgO and YBCO/LMO/homo-epi MgO/IBAD-MgO templates are similar. These results demonstrate the strong potential of using LMO as a single cap layer directly on IBAD-MgO for the development of a simplified IBAD architecture.",

keywords = "Buffers, Critical current density, IBAD-MgO, LMO, PLD-YBCO",

author = "{\"O} Polat and Tolga Aytug and Mariappan Paranthaman and Kyunghoon Kim and Yifei Zhang and Claudia Cantoni and Zuev, \{Yuri L.\} and Amit Goyal and Thompson, \{James R.\} and Christen, \{David K.\} and Xuming Xiong and Venkat Selvamanickam",

year = "2009",

month = jun,

doi = "10.1109/TASC.2009.2018815",

language = "English",

volume = "19",

pages = "3315--3318",

journal = "IEEE Transactions on Applied Superconductivity",

issn = "1051-8223",

publisher = "Institute of Electrical and Electronics Engineers Inc.",

number = "3",

}

TY - JOUR

T1 - Properties of YBCO on LaMnO3-capped IBAD MgO-templates without homo-epitaxial MgO layer

AU - Polat, Ö

AU - Aytug, Tolga

AU - Paranthaman, Mariappan

AU - Kim, Kyunghoon

AU - Zhang, Yifei

AU - Cantoni, Claudia

AU - Zuev, Yuri L.

AU - Goyal, Amit

AU - Thompson, James R.

AU - Christen, David K.

AU - Xiong, Xuming

AU - Selvamanickam, Venkat

PY - 2009/6

Y1 - 2009/6

N2 - Previously, it has been well established that in an IBAD architecture for coated conductors, (1) LaMnO3 (LMO) buffer layers are structurally and chemically compatible with an underlying homo-epitaxial MgO layer and (2) high current density YBCO films can be grown on these LMO templates. In the present work, the homo-epi MgO layer has been successfully eliminated and a LMO cap layer was grown directly on the IBAD-MgO template. The performance of the LMO/IBAD-MgO samples has been qualified by depositing 1 μm-thick YBCO coatings by pulsed laser deposition. Electrical transport measurements of YBCO films on the standard (with homo-epi MgO) and simplified (without homo-epi MgO) IBAD architectures were carried out. The angular dependence of critical current density (Jc) is similar for both IBAD architectures. XRD measurements indicate good, c-axis aligned YBCO films. Transmission electron microscopy (TEM) images reveal that microstructures of YBCO/LMO/IBAD-MgO and YBCO/LMO/homo-epi MgO/IBAD-MgO templates are similar. These results demonstrate the strong potential of using LMO as a single cap layer directly on IBAD-MgO for the development of a simplified IBAD architecture.

AB - Previously, it has been well established that in an IBAD architecture for coated conductors, (1) LaMnO3 (LMO) buffer layers are structurally and chemically compatible with an underlying homo-epitaxial MgO layer and (2) high current density YBCO films can be grown on these LMO templates. In the present work, the homo-epi MgO layer has been successfully eliminated and a LMO cap layer was grown directly on the IBAD-MgO template. The performance of the LMO/IBAD-MgO samples has been qualified by depositing 1 μm-thick YBCO coatings by pulsed laser deposition. Electrical transport measurements of YBCO films on the standard (with homo-epi MgO) and simplified (without homo-epi MgO) IBAD architectures were carried out. The angular dependence of critical current density (Jc) is similar for both IBAD architectures. XRD measurements indicate good, c-axis aligned YBCO films. Transmission electron microscopy (TEM) images reveal that microstructures of YBCO/LMO/IBAD-MgO and YBCO/LMO/homo-epi MgO/IBAD-MgO templates are similar. These results demonstrate the strong potential of using LMO as a single cap layer directly on IBAD-MgO for the development of a simplified IBAD architecture.

KW - Buffers

KW - Critical current density

KW - IBAD-MgO

KW - LMO

KW - PLD-YBCO

UR - https://www.scopus.com/pages/publications/68649095602

U2 - 10.1109/TASC.2009.2018815

DO - 10.1109/TASC.2009.2018815

M3 - Article

AN - SCOPUS:68649095602

SN - 1051-8223

VL - 19

SP - 3315

EP - 3318

JO - IEEE Transactions on Applied Superconductivity

JF - IEEE Transactions on Applied Superconductivity

IS - 3

M1 - 5153190

ER -

Properties of YBCO on LaMnO₃-capped IBAD MgO-templates without homo-epitaxial MgO layer

Abstract

Keywords

Access to Document

Other files and links

Fingerprint

Cite this