Noninvasive Temperature Measurement in Dental Materials Using Nd³⁺, Yb³⁺ Doped Nanoparticles Emitting in the Near Infrared Region

In this work, the application of near infrared (NIR)-emitting NaYbF₄:1%Tm³⁺@NaLuF₄:30%Nd³⁺ core–shell nanoparticles is reported for noninvasive probing and monitoring the temperature during photopolymerization of dental materials. When excited at 808 nm, the synthesized nanoparticles emit NIR photoluminescence (PL) with two distinctive peaks at 865 and 980 nm which correspond to radiative transitions from the doped Nd³⁺ and Yb³⁺ ions, respectively. Luminescence intensity ratio between these two bands is found to vary with temperature due to temperature-dependent electronic excitation energy transfer between Nd³⁺ and Yb³⁺ ions at the core/shell interface. This finding allows luminescence ratiometric evaluation of the in situ temperature during photopolymerization of resin cement (doped with nanoparticles) in a veneer placement procedure. In addition, the NIR emission also enables PL imaging of the distribution of the adhesive under the veneer. The results highlight that rare-earth ions–doped nanoparticles with both excitation and emission in the NIR spectral range are advantageous for both PL-based nanothermometry and imaging due to the reduced attenuation of NIR light by dental ceramics.