Interface and grain boundary structures in YBa₂Cu₃O_7-x and YBa₂Cu₄O₈ materials

Y₂BaCuO₅YBa₂Cu₃O_7-x (Y211/Y123) interfaces in melt-processed YBa₂Cu₃O_7-x were studied by high-resolution transmission electron microscopy and energy dispersive X-ray spectroscopy. Yttrium enrichment and barium depletion were observed locally at the Y211/Y123 interfaces where Y123 (001) facets were present. This effect may be interpreted as the result of lattice substitution of Ba by Y near these interfaces. Cation nonstoichiometry was found near Y211/Y123 interfaces where liquid phases (Cu-Ba-O) were present. This chemical disorder introduces numerous point defects in the Y123, and these defects may act as additional pinning sites alongwith stacking faults. A comparison of grain boundary (GB) chemical composition in polycrystalline YBa₂Cu₃O_7-x and YBa₂Cu₄O₈(Y124), studied using nanoprobe parallel-detection electron energy-loss spectroscopy (EELS), is presented. The studies of Y124 show that stoichiometric grain boundaries can also form weak links between superconducting grains. It is suggested that weak-link behavior is determined largely by misorientation at grain boundaries.