Influence of additional adhesive application on the microtensile bond strength of adhesive systems

This study evaluated microtensile bond strength (μTBS) when an additional adhesive layer was applied to the dentin surface. Thirty-five human third molars were flattened to expose the occlusal dentin surface. The teeth were randomly assigned to 7 experimental groups: G1-Single Bond (SB); G2-additional layer of SB; G3-a layer of Scotchbond Multi-purpose (SMP) adhesive applied over SB; G4-Clearfil SE Bond (CE); G5-additional layer of CE; G6-Adper Prompt (AP) and G7-additional layer of AR For the G2, G3, G5 and G7 groups, the first adhesive layer was light-cured before application of the additional layer. After bonding procedures, 5-mm high composite crowns were incrementally built up. The samples were sectioned to obtain 0.9 × 0.9 beams, which were tested under tension at a crosshead speed of 0.5-mm/minute until failure. The failure mode and adhesive thickness were evaluated under SEM. The μTBS data were analyzed by 1-way ANOVA and post-hoc Ducan's Test (α=0.05). Mean adhesive thickness was analyzed by 1-way ANOVA and post-hoc Tukey's test (α=0.05). The results indicated that G3 presented the highest μTBS and the thickest adhesive layer. G6 and G7 presented the lowest μTBS values. When solvent-free adhesives systems were used, μTBS values were not affected by the thicker layer.