Influence of a light-activated glaze on the adhesion of Streptococcus sanguinis to the surface of polymers used in fabrication of interim prostheses

AIM: This study aimed to investigate the adhesion of Streptococcus sanguinis to the surface of interim prostheses that were treated or not treated with a light-activated glaze, and subjected or not subjected to a thermocycling procedure. METHODS: 36 specimens of each resin were divided into 4 groups: heat-activated acrylic resin; chemically-activated acrylic resin; bis-acryl composite resin (Protemp; 3M ESPE); and bis-GMA (Charisma; Heraeus Kulzer). Half of the specimens underwent application of glaze and the other half underwent mechanical polishing. Specimens were randomly distributed into groups (N = 9) with and without thermocycling (2000 cycles). Surface energy, roughness and microbiological analyses were performed. RESULTS: Groups treated with glaze showed lower roughness when compared with the same groups without glaze treatment, before and after thermocycling, except for the bis-acryl groups after thermocycling. Surface energy values were higher in the groups treated with glaze, except the bis-acryl group before and after thermocycling. After thermocycling, the values of bacterial adhesion decreased numerically, with the exception of the chemically-activated acrylic resin group treated with glaze and the heat-activated acrylic resin group without glaze treatment. CONCLUSION: The application of glaze and the thermocycling do not influence, in a statistically significant manner, the bacterial adhesion on polymer surfaces.