Electro-catalytic oxidation of CO on Pt catalyst supported on carbon nanotubes pretreated with oxidative acids

Characteristics of nanosized Pt electro-catalyst deposited on carbon nanotubes (CNTs) were studied with CO-stripping voltammogram and chronoamperometry measurements. The CNTs were pretreated by oxidation in HNO₃, mixed HNO₃ + H₂SO₄ and H₂SO₄ + K₂Cr₂O₇ solution, respectively, to enable surface modification. Well-homogenized Pt particles (average size: ≈3 nm) were loaded onto the pretreated CNT samples by a modified colloidal method. TEM, BET, FTIR and XRD techniques were used to characterize the physicochemical properties of the pretreated CNT samples. In the electro-oxidation of CO, all the Pt/CNT samples showed lower on-set as well as peak potentials than the conventional Pt/XC-72 electro-catalyst, indicating that the Pt/CNT samples were more resistant to CO poisoning and could be superior anode electro-catalyst for the proton exchange membrane fuel cells (PEMFCs). Moreover, we found that the pretreatment of CNTs in mixed HNO₃ + H₂SO₄ solution was very beneficial for the performance enhancement of Pt/CNT electro-catalyst; the catalyst obtained as such gave the lowest peak potential and the highest catalytic activity for the electro-oxidation of CO. Larger amount of oxygen-containing functional groups, higher percentage of mesopores, and higher graphitic crystallinity of the pretreated CNTs were considered crucial for the performance enhancement, e.g., by strengthening the interaction between Pt nanoparticles and the CNT support and enhancing the mass diffusion in the electro-chemical reaction.