Effect of universal adhesives and self-etch ceramic primers on bond strength to glass-ceramics: A systematic review and meta-analysis of in vitro studies

Statement of problem: To simplify dental procedures, multicomponent products such as universal adhesives and self-etch ceramic primers have been recommended for glass-ceramic bonding; however, studies have shown a wide range of results. Purpose: The purpose of this systematic review and meta-analysis was to analyze the in vitro bond strength promoted by hydrofluoric acid+silane-containing universal adhesives and a self-etch ceramic primer to glass-ceramics and compare it with that of conventional treatments. Material and methods: A systematic search was conducted in the PubMed/Medline, Scopus, LILACS, and ISI Web of Science databases up to April 2021. In vitro studies assessing the resin-mediated bond to glass-ceramics by using a self-etch ceramic primer and hydrofluoric acid+silane-containing universal adhesives and/or compared with traditional hydrofluoric acid+glass-ceramic primers were included. Selection of studies, data extraction, and risk-of-bias analysis were performed. Statistical analysis was performed by using a review management software program using a random effects model (α=.05). Results: A total of 33 studies were included in the qualitative analysis and 26 studies in the quantitative analysis. Bond strength to lithium disilicate ceramic was higher when a hydrofluoric acid+glass-ceramic primer was used than when using a hydrofluoric acid+silane-containing universal adhesive (P<.05), except when 9% to 10% acid concentration was used in combination with static aging (P=.100). A self-etch ceramic primer promoted bond strength values to lithium disilicate that were similar to those of the hydrofluoric acid+glass-ceramic primer (P>.100). Conclusions: Hydrofluoric acid+silane-containing universal adhesive was not as effective as the hydrofluoric acid+glass-ceramic primer in promoting bond strength to glass-ceramic. Bond strength values generated by a self-etch ceramic primer to glass-ceramic were similar to those generated by the conventional treatment.